Table of Physical Property
Type | MC Nylon | POM-C Nat POM-C Bk |
U-PE100 | PET | PC | HDPE | PPS | PP | PVC-U | DURATRON Polyimide |
PBI | ABS | PEEK | ULTEM | ESD Plastic Production |
PVDF | TORLON | Test Method ASTM |
||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Item | Unit | MC901 Blue MC907 I/V |
PET 100 |
XP | PEEK-1000 | ULTEM-1000 | ESD225 | TR-4203 | ||||||||||||
Specific Gravity | g/cm2 | 1.15~1.17 | 1.41 | 0.94 | 1.39 | 1.22 | 0.95 | 1.35 | 0.91 | 1.43 | 1.40 | 1.30 | 1.07 | 1.32 | 1.27 | 1.33 | 1.79 | 1.41 | D-792 | |
Tensile Strength | Mpa [kgf/cm2] |
78-96 [800~980] |
61 [620] |
31 [320] |
84 [860] |
70 [705] |
22 [230] |
93 [950] |
30 [360] |
46 [470] |
92 [940] |
160 [1630] |
49 [500] |
98 [1000] |
124 [1260] |
42 [430] |
50 [510] |
120 [1500] |
D-638 | |
Elongation | % | 10~50 | 40 | 500 | 32 | 125 | 600 | 19 | 30 | 3 | 4 | 3 | 30 | 20 | 23 | 15 | 30 | 10 | D-638 | |
Tensile Modulus | MPa [103kgf/cm2] |
2942~3432 [30~35] |
2824 [28.8] |
- | - | 2400 [24.5] |
932 [9.5] |
3447 [35.15] |
1177 [21] |
2942 [30] |
- | 5800 [59] |
- | - | - | 1500 [16] |
2300 [24] |
4500 [46] |
D-638 | |
Compressive Strength | Yield Point | MPa [10kgf/cm2] |
92~103 [940~1050] |
- | - | - | - | - | - | - | - | - | - | - | - | - | - | - | - | D-695 |
5% Deformation [10% Deformation] |
MPa [10kgf/cm2] |
92~95 [940~970] |
103 [1050] |
20 [200] |
97 [990] |
72 [710] |
29 [300] |
107 [1100] |
49 [500] |
76 [780] |
110 [1130] |
156 [1590] |
- | 119 [1210] |
118 [1200] |
44 [450] |
- | 117 [1200] |
D-695 | |
Bending Strength | MPa [kgf/cm2] |
96~110 [980~1120] |
89 [910] |
20 [200] |
127 [1300] |
108 [1100] |
- | 147 [1500] |
- | - | 131 [1340] |
220 [2240] |
- | 170 [1730] |
157 [1600] |
49 [500] |
- | 196 [2000] |
D-790 | |
Flexural Modulus | MPa [103kgf/cm2] |
2942~3530 [30~36] |
2589 [26.4] |
883 [9] |
3011 [30.7] |
395 [23.5] |
- | 3430 [35] |
- | - | 3430 [35] |
6460 [66] |
190 [50] |
4021 [41] |
3040 [31] |
1370 [14] |
2200 [22.5] |
3620 [37] |
D-790 | |
IZOD Notched Impact Value |
J/m [kgf·cm2/2.54cm] |
35~50 [9~13] |
74 [19.1] |
- | 48 [12.4] |
80 [19.5] |
89 [23] |
19 [5] |
30 [10] |
9.7 [2.5] |
34 [9] |
46 [12] |
- | 77 [20] |
42 [11] |
77 [20] |
63 [20] |
138 [36] |
D-256 | |
Rockwell Hardness | R-Scale | 115~125 | 119 | 52 | 125 | - | 54 | 124 | 110 | - | 126 | 129 | 77 | 120 | 128 | 111 | 118 | 127 | D-785 | |
Shore Hardness | D type | 84~86 | 78 | - | 93 | 83 | 60 | 97 | 77 | 53 | 113 | 138 | - | 105 | 116 | 55 | 75 | 119 | D-785 | |
Melting Point | ℃ | 220~223 | 165 | - | 252 | - | 120 | 282 | 120 | 75 | - | - | - | 340 | - | 165 | 175 | - | - | |
Thermal Deflection Temperature |
0.445MPa [4.6kgf/cm2] |
℃ | 220~215 | 158 | 89 | 194 | 142 | 65 | - | 105 | - | - | - | - | - | 210 | - | 149 | - | D-648 |
1.820MPa [18.6kgf/cm2] |
℃ | 160~200 | 110 | 54 | 98 | 132 | 47 | 121 | 80 | - | 360 | 435 | - | 150 | 200 | 106 | 105 | 280x | D-648 | |
Coefficient of Linear Expansion | x105/℃ | 9.0 | 9.0 | 20.0 | 6.0 | 6 | 15 | 5.0 | 11 | 8 | 3.6 | 2.5 | - | 5.0 | 5.6 | 15 | 13.0 | 3.0 | D-696 | |
Absorption Rate | Underwater, Equilibrium | % | 5.5~7.0 | 0.7 | - | 0.55 | 0.15 | 0.01 | - | 0.01 | 0.2 | - | 0.5 | - | 0.5 | - | 5.0 | - | - | D-570 |
Underwater, 24hrs | 0.5~1.0 | 0.22 | - | 0.07 | 0.3 | 0.01 | 0.1 | 0.01 | - | 0.40 | - | - | 0.14 | 0.25 | 0.8 | 0.01 | 0.29 | |||
Volume Resistivity | Ω·m | 4.2x1013 | 1x1012 | >1011 | >1014 | >1013 | >1014 | >1014 | >1014 | >1013 | >1013 | >1013 | - | >1014 | >1011 | 106~1010 | >1013 | >1015 | D-257 | |
4.2x1018 | 1x1014 | >1013 | >1016 | >1015 | >1016 | >1016 | >1016 | >1015 | >1015 | >1015 | - | >1016 | >1013 | 1010~1012 | >1015 | >1017 | ||||
Dielectric Breakdown Voltage | kv/mm | 18~22 | 20 | - | 60 | 28 | 40 | 21.3 | - | - | 18.0 | 23 | - | 19 | 33 | - | 18 | 23.6 | D-149 | |
Permittivity 106Hz | - | 3.7 | 3.7 | - | 3.2 | 3 | - | 3.0 | - | - | 3.59 | 3.4 | - | 3.3 | 3.15 | - | 6.0 | 4.2 | D-150 | |
Dissipation factor 106Hz | - | 0.02 | 0.007 | - | 0.02 | 0.001 | - | 0.0013 | - | - | 0.0012 | 0.000 | - | 0.003 | 0.0013 | - | 0.165 | 0.023 | D-150 | |
Combustibility | - | V-2 | HB | - | HB | HB | HB | V-0 | HB | V-0 | V-0 | V-0 | HB | V-0 | V-0.5V | HB | V-0 | V-0 | (UL94) |
Material Selection Table
Types | Continuous Use Temperature High Temperature(℃) Low Temperature(℃) |
Chemical Resistance Oil Acid Alkali Organic Solvent |
Food Sanitation Act |
Water Vapor Resistance |
Water Resistance | Abrasion Resistance W Slide wear A Scratch wear |
Dimensional Stability |
Impact Resistance | Material property | Main Industries |
---|---|---|---|---|---|---|---|---|---|---|
MC Nylon MC901 Blue MC907 I/V |
120 | O | Conformity | X | △ | Both W and A excellent under severe service condition | Not so good | Good | Abrasion Resistance·Excellent wear resistance and self-lubricating, widely available material. Large-scale material accessible |
Construction machinery, industrial machinery transportation machinery, steel machinery |
X | ||||||||||
-40 | O~△ | |||||||||
O | ||||||||||
MC Nylon MC501 |
120 | O | Conformity | X | △ | Both W and A excellent under severe service condition | Not so good | Good | Material giving conductivity to MCD abrasion resistance ·self-lubricating maintaining the characteristics of original MC |
IC-related, water-soluble car paint system System LCD industry, transportation machine |
X | ||||||||||
- | O~△ | |||||||||
O | ||||||||||
Acetal co-polymer POM-C |
95 | O | Conformity | X | O | Good | Good | Good | Less absorbency and strength. Good fatigue resistence. General purpose mechanical parts. good processability |
Food processing machine, packing machine, vending machine, transportation machine |
△~X | ||||||||||
-60V | O | |||||||||
O | ||||||||||
supermolecular PE U-PE100 |
80 | O | Conformity | X | O | Both W and A excellent at room temperature and low weight | Not so good | Super excellent |
Excellent friction properties under the conditions of room temperature and low weight. wear resistance, FDA-approved, optimum for a splash of water |
Food processing machinery, packaging machinery, paper machinery transportation machinery |
O | ||||||||||
-100 | O | |||||||||
O | ||||||||||
Polyethylene terephthalate PET100 |
80 | O | Conformity | X | O | Both W and A excellent at room temperature and low weight | Excellent | Not so good | Good dimensional stability, and optimal for parts that require high precision. Optimal for food machine parts, FDA-approved, slightly poor impact |
Food processing machinery, packaging machinery, electric·and electronic field |
Weak acid O | ||||||||||
- | X | |||||||||
O~△ | ||||||||||
Polycarbonate PC |
110 | O | Conformity | X | O | Both W and A excellent at room temperature and low weight | Excellent | Excellent | High impact strength maintenance at low temperature, dimensional stability, suitable for food contact | Food processing machinery, optical components, electric·and electronic field |
Weak acid O | ||||||||||
-60 | X | |||||||||
X | ||||||||||
High density polyethylene HDPE |
80 | O | Comformity | X | O | Both W and A excellent at room temperature and low weight | Not so good | Good | No deformation during cutting work and use, hygienic, wear resistance |
Food processing machinery, packaging machinery |
O | ||||||||||
-100 | O | |||||||||
O | ||||||||||
Polypropylene PP |
- | O | Conformity | △ | △ | Good | Good | Good | Lightweight and excellent surface gloss. Excellent heat resistance and electrical properties. Good molding processability. |
Light electrical appliance, industrial machinery, automobile parts |
◎ | ||||||||||
- | O | |||||||||
O | ||||||||||
Rigid polyvinyl chloride PVC-U |
60 | O | Conformity | O | O | Good | Good | Normal | Maintain high rigidity and high hardness at room temperature. | Plating equipment, industrial machinery |
O | ||||||||||
-20 | O | |||||||||
O | ||||||||||
ABS | 85 | ◎ | Conformity | O | O | Good | Good | Good | Excellent impact resistance and crack resistance at low temperature. No process deformation. Easy adhesion. |
Material for model production |
◎ | ||||||||||
-40 | ◎ | |||||||||
◎ | ||||||||||
PEEK Noraml grade PEEK-100 |
250 | O | Conformity | ◎ | O | Good | Good | Normal | Super engineering plastic with excellent heat resistance and chemical resistance. Excellent mechanical properties at high temperature. |
Semiconductor LCD industry industrial equipment, physics and chemical devices |
O | ||||||||||
-50 | O~△ | |||||||||
O | ||||||||||
ULTEM UL-100 |
170 | O | Conformity | ◎ | O | Not so good | Good | Not so good | High strength and excellent electrical characteristics at high temperature. Not so good wear resistance. |
Food machinery, medical equipment, electrical insulation, insulation |
X | ||||||||||
- | O~X | |||||||||
OX | ||||||||||
TORLON TR-4203 |
250 | ◎ | Conformity | X | △ | Good | Good | Good | Excellent mechanical properties and durability at high temperature. Low coefficient of linear expansion. Flame retardancy, absorbency. |
industrial machinery, office equipment, chemical plant, Semiconductor LCD industry |
O~◎ | ||||||||||
-190 | X~△ | |||||||||
O~◎ | ||||||||||
PVDF | 150 | ◎ | Conformity | ◎ | ◎ | Normal | Normal | Good | Excellent mechanical properties among fluorine-based materials. Excellent flame-resistance, weather resistance, and radiation resistance. |
Semiconductor LCD industry chemical equipment, medical equipment , Food processing machinery |
O~◎ | ||||||||||
-50 | △~O | |||||||||
X~O | ||||||||||
Polyimide XP |
304 | ◎ | - | X | △ | Good | Good | Not so good | Higher heat resistant than TORLON. Mechanical Properties at high temperature, excellent durability. No impurities and flame retardant. |
Semiconductor LCD industry precision machinery, nuclear industry aerospace |
X~△ | ||||||||||
- | △~O | |||||||||
O~◎ | ||||||||||
MC nylon MC-R6 |
220 | ◎ | - | ◎ | ◎ | Normal | Good | Not so good | The only PPS that can be used without glass fiber reinforcement, excellent chemical resistance, excellent dimensional stability, flammability. |
Semiconductor LCD industry chemical devices, physics and chemical devices |
◎ | ||||||||||
-20 | ◎ | |||||||||
◎ | ||||||||||
PBI | 345 | ◎ | Conformity | X | △ | Good | Good | Not so good | Because it is a compression molded product of polybenzimidazole resin, it has the highest heat resistance and mechanical strength among commercialized plastics. | Semiconductor LCD industry precision machinery, nuclear power industry, aerospace |
X~△ | ||||||||||
- | △~X | |||||||||
O~◎ |